NURGIANSYAH, RAMA (2025) PENGARUH KANDUNGAN SERBUK SEKAM PADI, SERBUK KULIT KACANG TANAH DAN SERAT IJUK TERHADAP KEKUATAN IMPAK DAN MIKROSTRUKTUR KOMPOSIT MATRIK RESIN. S1 thesis, Universitas Mercu Buana Jakarta.
|
Text (HAL COVER)
01 COVER.pdf Download (356kB) | Preview |
|
![[img]](https://repository.mercubuana.ac.id/style/images/fileicons/text.png) |
Text (BAB I)
02 BAB 1.pdf Restricted to Registered users only Download (130kB) |
|
|
Text (BAB II)
03 BAB 2.pdf Restricted to Registered users only Download (334kB) |
|
|
Text (BAB III)
04 BAB 3.pdf Restricted to Registered users only Download (469kB) |
|
|
Text (BAB IV)
05 BAB 4.pdf Restricted to Registered users only Download (666kB) |
|
|
Text (BAB V)
06 BAB 5.pdf Restricted to Registered users only Download (27kB) |
|
|
Text (DAFTAR PUSTAKA)
07 DAFTAR PUSTAKA.pdf Restricted to Registered users only Download (132kB) |
|
|
Text (LAMPIRAN)
08 LAMPIRAN.pdf Restricted to Registered users only Download (845kB) |
Abstract
This study is driven by the utilization of organic materials of rice husk powder, peanut shell powder, and palm fiber for the needs of environmentally friendly composite materials. This research seeks to ascertain the largest percentage within the impact test resistance of each material and the characteristics of the composite microstructure. This research was conducted using the experimental test method at Mercu Buana University’s Mechanical Engineering Laboratory, where the examination is carried there was an utilizing the Charpy to test the impact method, while the microstructure characteristics were carried out using optical microscopy (OM). The experiment was employed in this investigation by dividing into 9 composition variations on the impact test specimen by manual molding using a specimen mold and drying it under sunlight for 1-2 hours, after which an impact test was conducted in order to assess the durability of the specimen and analyze the microstructure of the specimen. Based on the studies that have been conducted, the specimen with the highest toughness is combination B which has a toughness value of 20 kJ/m2 Keywords: Impact test, microstructure, rice husk powder, peanut shell powder, palm fiber. Penelitian ini dilatar belakangi pemanfaatan bahan organik serbuk sekam padi, serbuk kulit kacang tanah, dan serat ijuk untuk kebutuhan mataerial komposit yang ramah lingkungan. Penelitian ini bertujuan untuk mengetahui prosentase yang paling besar dalam ketahanan uji impak dari setiap bahannya dan karakteristik mikrostruktur komposit. Penelitian ini dilakukan dengan metode uji eksperimen di Laboratorium Teknik Mesin Universitas Mercu Buana, dimana pengujian yang dilakukan adalah uji impak dengan menggunakan metode charpy, sementara karakteristik mikrostruktur dilakukan menggunakan optical microscopy (OM). Percobaan yang digunakan dalam penelitian ini, dilakukan dengan cara membagi menjadi 9 variasi komposisi pada specimen uji impak dengan pencetakan manual menggunakan cetakan spesimen dan dikeringkan dibawah sinar matahari selama 1-2 jam, setelahnya dilakukan pengujian impak untuk mengetahui ketangguhan dari spesimen dan menganalisis struktur mikro dari spesimen. Berdasarkan penelitian yang telah dilakukan, spesimen yang memiliki ketangguhan tertinggi adalah kombinasi B yang memiliki nilai ketangguhan 20 kJ/m2 Kata kunci : Uji impak, mikrostruktur, serbuk sekam padi, serbuk kulit kacang tanah, serat ijuk.