MUDA, ARIS (2020) ANALISIS PENGARUH VARIASI KONSENTRASI KATALIS TERHADAP KEKUATAN IMPAK KOMPOSIT RESIN EPOXY DIPERKUAT SERAT SABUT KELAPA. S1 thesis, Universitas Mercu Buana Bekasi.
|
Text
1.Halaman Judul.pdf Download (211kB) | Preview |
|
|
Text
2.Abstrak.pdf Download (205kB) | Preview |
|
|
Text
4.Surat Pernyataan.pdf Download (733kB) | Preview |
|
|
Text
5.Surat Pengesahan.pdf Download (630kB) | Preview |
|
|
Text
5.Kata Pengantar.pdf Download (276kB) | Preview |
|
|
Text
6.Daftar Isi.pdf Download (203kB) | Preview |
|
|
Text
7.Daftar Tabel.pdf Download (199kB) | Preview |
|
|
Text
8.Daftar Gambar.pdf Download (200kB) | Preview |
|
|
Text
9. Daftar Lampiran.pdf Download (198kB) | Preview |
|
![[img]](https://repository.mercubuana.ac.id/style/images/fileicons/text.png) |
Text
10.Bab 1.pdf Restricted to Registered users only Download (214kB) |
|
|
Text
11.Bab 2.pdf Restricted to Registered users only Download (527kB) |
|
|
Text
12.Bab 3.pdf Restricted to Registered users only Download (568kB) |
|
|
Text
13.Bab 4.pdf Restricted to Registered users only Download (773kB) |
|
|
Text
14.Bab 5.pdf Restricted to Registered users only Download (208kB) |
|
|
Text
15.Daftar Pustaka.pdf Restricted to Registered users only Download (253kB) |
|
|
Text
16.Lampiran.pdf Restricted to Registered users only Download (1MB) |
Abstract
ABSTRAK Seiring dengan perkembangan jaman, kebutuhan akan material polimer sebagai bahan utama dalam dunia industri semakin meningkat. Untuk menghasilkan produk yang berkualitas dibutuhkan bahan yang cocok untuk membuat produk tersebut. Polimer memiliki keunggulan dibandingkan logam dan kayu, karena tahan terhadap korosi, bersifat isolator, elastis dan biaya pembuatannya murah. Kemudian polimer dikembangkan menjadi komposit yang terbentuk dari kombinasi dua atau lebih material yang mempunyai sifat mekanik lebih unggul dari material pembentuknya. Tujuan penelitian ini adalah mengetahui pengaruh konsentrasi katalis dan komposisi ideal terhadap kekuatan impak yang maksimal. Metode penelitian ini menggunakan standar ISO 179-1:2010 sebagai acuan untuk pembuatan spesimen, bahan yang dipilih untuk membuat spesimen yaitu resin epoxy dan serat sabut kelapa sebagai penguat. Hasil dari penelitian pada komposit dengan 65% katalis (hardener) dihasilkan kekuatan impak rata-rata 50,31 kJ/m2 , komposit dengan 55% katalis (hardener) dihasilkan kekuatan impak rata-rata 13,44 kJ/m2 , komposit dengan 45% katalis (hardener) dihasilkan kekuatan impak rata-rata 11,33 kJ/m2 , komposit dengan 35% katalis (hardener) dihasilkan kekuatan impak rata-rata 23,83 kJ/m2 , maka kompisi ideal untuk mendapatkan hasil kekuatan impak komposit resin epoxy diperkuat serat sabut kelapa yang tinggi adalah dengan perbandingan rasio fraksi massa 30% epoxy, 65% katalis (hardener), dan 5% serat. Terbukti bahwa dengan komposisi tersebut diperoleh kekuatan impak tertinggi sebesar 50,31 kJ/m2 . untuk validasi data yang dihasilkan dari penelitian ini dilakukan uji regresi. Kata kunci: Resin, Katalis, Serat, Kekuatan Impak ANALYSIS OF THE EFFECT OF VARIATIONS IN CATALYST CONCENTRATION ON THE IMPACT STRENGTH OF EPOXY RESIN COMPOSITE REINFORCED COCONUT FIBER ABSTRACT Along with the changing times, the need for polymeric materials as the main material in the industrial world is increasing. To produce a quality product, suitable materials are needed to make the product. Polymers have advantages over metals and wood, because they are resistant to corrosion, are insulating, elastic and have low manufacturing costs. Then the polymer is developed into a composite that is formed from a combination of two or more materials that have mechanical properties superior to the forming material. The purpose of this study was to determine the effect of catalyst concentration and ideal composition on maximum impact strength. This research method uses ISO 179-1: 2010 standard as a reference for making specimens, the material chosen to make specimens is epoxy resin and coconut fiber as reinforcement. The results of research on composites with 65% catalyst (hardener) produced an average impact strength of 50,31 kJ / m2 , composites with 55% catalyst (hardener) produced an average impact strength of 13,44 kJ / m2 , composites with 45% catalyst (hardener) produced an average impact strength of 11,33 kJ / m2 , a composite with 35% catalyst (hardener) produced an average impact strength of 23,83 kJ / m2 , hence an ideal composition to obtain the impact strength of a reinforced epoxy resin composite coconut fiber fiber is high with a ratio of 30% epoxy mass fraction ratio, 65% catalyst (hardener), and 5% fiber. It was proven that with this composition the highest impact strength was obtained at 50,31 kJ / m2 . To validate the data generated from this study, a regression test was performed. Keywords: Resin, catalyst, Fiber, Impact Strength
| Item Type: | Thesis (S1) |
|---|---|
| Call Number CD: | FT/MSN 20 007 |
| NIM/NIDN Creators: | 41315320020 |
| Uncontrolled Keywords: | Kata kunci: Resin, Katalis, Serat, Kekuatan Impak |
| Subjects: | 000 Computer Science, Information and General Works/Ilmu Komputer, Informasi, dan Karya Umum > 000. Computer Science, Information and General Works/Ilmu Komputer, Informasi, dan Karya Umum > 006 Special Computer Methods/Metode Komputer Tertentu > 006.3 Artificial Intelligence/Kecerdasan Buatan > 006.31 Machine Learning/Pembelajaran Mesin |
| Divisions: | Pascasarjana > Magister Teknik Mesin |
| Depositing User: | siti maisyaroh |
| Date Deposited: | 09 Mar 2022 05:12 |
| Last Modified: | 09 Mar 2022 05:12 |
| URI: | http://repository.mercubuana.ac.id/id/eprint/57588 |
Actions (login required)
 |
View Item |