SINTESA KOMPOSITE BaCO3/6Fe2O3/C DAN KARAKTERISASINYA

SISWANTO, MUHAMMAD ALIF (2017) SINTESA KOMPOSITE BaCO3/6Fe2O3/C DAN KARAKTERISASINYA. S1 thesis, Universitas Mercu Buana Jakarta.

[img]
Preview
 Text (ABSTRAK)
Abstrak.pdf
Download (103kB) | Preview
[img]
Preview
 Text (HAL COVER)
Hal Cover.pdf
Download (386kB) | Preview
[img] Text (BAB I)
BAB I.pdf
Restricted to Registered users only
Download (173kB)
[img] Text (BAB II)
BAB II.pdf
Restricted to Registered users only
Download (621kB)
[img] Text (BAB III)
BAB III.pdf
Restricted to Registered users only
Download (362kB)
[img] Text (BAB IV)
BAB IV.pdf
Restricted to Registered users only
Download (304kB)
[img] Text (BAB V)
BAB V.pdf
Restricted to Registered users only
Download (106kB)
[img] Text (DAFTAR PUSTAKA DAN LAMPIRAN)
Hal Daftar Pustaka & Lampiran.pdf
Restricted to Registered users only
Download (798kB)

Abstract

Dalam penelitian ini, telah dibuat komposit BaCO3/6Fe2O3/C dari bahan barium karbonat (BaCO3), Hematit (Fe2O3), dan Karbon Aktif (C) menggunakan teknik High Energy Milling (HEM) dengan variasi waktu sintering 750oC, 950oC, 1050oC, dan 1200oC. Perbandingan komposisi serbuk BaCO3/6Fe2O3 + C adalah 9 : 1. Proses milling menggunakan metode wet milling dengan ethanol sebagai media. Karakterisasi yang dilakukan meliputi analisis struktur kristal dengan X-Ray Powder Diffraction (XRD), dan sifat kemagnetan dengan Vibrating Sample Magnetometer (VSM). Hasil dari analisis XRD menunjukkan bahwa telah terbentuk struktur komposit BaCO3/6Fe2O3/C dengan hasil unsur yang terbentuk adalah BaFe12O19. Dimana barium heksaferit memiliki struktur kristal hexagonal dengan parameter kisi a = 5.038 Å dan c = 14.539 Å. Sedangkan Fe2O3 mempunyai struktur kristal cubic dengan parameter kisi a = 5.025 Å dan c = 13.658 Å. Dari analisis VSM, kondisi optimum komposit BaCO3/6Fe2O3/C dicapai pada proses sintering 1200oC dengan mangnetisasi saturasi (Ms) = 3.87 emu/g, magnetisasi remanen (Mr) = 1.37 emu/g dan koersivitas (Hc) 741.28 Oe. Kata kunci : Magnetik Komposit, Barium Karbonat, Hematit, Barium Heksaferit dan Karbon Aktif, High Energy Milling.

Item Type: Thesis (S1)
Call Number CD: FT/MSN. 18 091
NIM/NIDN Creators: 41312010027
Uncontrolled Keywords: Magnetik Komposit, Barium Karbonat, Hematit, Barium Heksaferit dan Karbon Aktif, High Energy Milling.
Subjects: 500 Natural Science and Mathematics/Ilmu-ilmu Alam dan Matematika > 530 Physics/Fisika > 538 Magnetism/Magnetisme
500 Natural Science and Mathematics/Ilmu-ilmu Alam dan Matematika > 530 Physics/Fisika > 538 Magnetism/Magnetisme > 538.3 Magnetic Properties/Sifat-sifat Magnet
500 Natural Science and Mathematics/Ilmu-ilmu Alam dan Matematika > 530 Physics/Fisika > 538 Magnetism/Magnetisme > 538.4 Magnetic Phenomena/Fenomena Magnet
600 Technology/Teknologi > 620 Engineering and Applied Operations/Ilmu Teknik dan operasi Terapan > 621 Applied Physics/Fisika terapan > 621.3 Electrical Engineering, Lighting, Superconductivity, Magnetic Engineering, Applied Optics, Paraphotic Technology, Electronics Communications Engineering, Computers/Teknik Elektro, Pencahayaan, Superkonduktivitas, Teknik Magnetik, Optik Terapan, Tekn
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: Dede Muksin Lubis
Date Deposited: 28 Dec 2017 02:25
Last Modified: 31 Oct 2018 08:29
URI: http://repository.mercubuana.ac.id/id/eprint/40042

Actions (login required)

View Item View Item
UMB Repository is powered by EPrints 3 which is developed by the School of Electronics and Computer Science at the University of Southampton. More information and software credits.